We use the PA6 GF20 material in the following processes：
- plastic injection moulding
- thermoplastic structure foaming (TSF)
PA6 GF20 Material Datasheet:
| 特性Property | 测试方法Test Method | 测试条件Test Condition | 单位Unit | 注塑级增强PA6GF20 |
|---|---|---|---|---|
| 引张强度Tensile Strength | ISO 527 |
50 mm/min.
|
MPa
|
145
|
| 断裂伸长率Elongation at Break | ISO 527 |
50 mm/min.
|
%
|
3.3
|
| 弯曲强度Flexural Strength | ISO 178 |
2 mm/min.
|
MPa
|
196
|
| 弯曲弹性率Flexural Modulus | ISO 178 |
2 mm/min.
|
MPa
|
5468
|
| 简支梁缺口冲击强度Charpy Impact notched | ISO 179 |
– |
KJ/m² |
10.6 |
| 简支梁无缺口冲击强度Charpy Impact Unotched | ISO 179 |
–
|
KJ/m²
|
82.5
|
| 洛氏硬度Rockwell Hardness | ISO 2039/2 |
–
|
–
|
117
|
| 密度Density | ISO 1183 |
23 °C
|
g/cm³
|
1.27
|
| 熔点Melting Point | ISO 3146C |
–
|
°C
|
220
|
| 热变形温度H.D.TAnnealedUnannealed | ISO 75 |
0.45 MPa 1.81 MPa
|
°C
|
– 199 |
| 燃烧率Flammability | UL94 |
–
|
–
|
HB
|