We use the PA66 GF40 material in the following processes：
- plastic injection moulding
- thermoplastic structure foaming (TSF)
PA66 GF40 Material Datasheet:
| 特性Property | 测试方法Test Method | 测试条件Test Condition | 单位Unit | 注塑级增强PA66GF40 |
|---|---|---|---|---|
| 引张强度Tensile Strength | ISO 527 |
50 mm/min.
|
MPa
|
226
|
| 断裂伸长率Elongation at Break | ISO 527 |
50 mm/min.
|
%
|
2.8
|
| 弯曲强度Flexural Strength | ISO 178 |
2 mm/min.
|
MPa
|
329
|
| 弯曲弹性率Flexural Modulus | ISO 178 |
2 mm/min.
|
MPa
|
11675
|
| 简支梁缺口冲击强度Charpy Impact notched | ISO 179 |
– |
KJ/m² |
16.9 |
| 简支梁无缺口冲击强度Charpy Impact Unotched | ISO 179 |
–
|
KJ/m²
|
99.8
|
| 洛氏硬度Rockwell Hardness | ISO 2039/2 |
–
|
–
|
119
|
| 密度Density | ISO 1183 |
23 °C
|
g/cm³
|
1.44
|
| 熔点Melting Point | ISO 3146C |
–
|
°C
|
260
|
| 热变形温度H.D.TAnnealed Unannealed | ISO 75 |
0.45 MPa 1.81 MPa
|
°C
|
– 258.4 |
| 燃烧率Flammability | UL94 |
–
|
–
|
HB
|